尼龙PA6本色加纤15%高流动 日本东丽CM1011G-15
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||
| 基本性能 | 吸水率 | 23℃，24小时 | ASTM D-570 |
|
% | ||
| 物理性能 | 泰伯磨耗量 | (1000g,CS-17)23℃ | ASTM D-1044 |
|
mg/1000次 | ||
| 比重 | ASTM D-792 |
|
|||||
| 机械性能 | 抗剪强度 | 80℃ | ASTM D-732 |
|
Kg/cm2 | ||
| IZOD冲击强度 | V-缺口1/2，23℃ | ASTM D-256 |
|
kg·cm/cm2 | |||
| 抗拉屈服强度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||
| 抗剪强度 | 23℃ | ASTM D-732 |
|
Kg/cm2 | |||
| 断裂伸长率 | 23℃ | ASTM D-638 |
|
% | |||
| 挠曲模量 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
M-标度 | |||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
R-标度 | |||
| 抗拉断裂强度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||
| 断裂伸长率 | -40℃ | ASTM D-638 |
|
% | |||
| 断裂伸长率 | 80℃ | ASTM D-638 |
|
% | |||
| 挠曲强度 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||
| 挠曲强度 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||
| 挠曲强度 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||
| 抗拉屈服强度 | -40℃ | ASTM D-638 |
|
Kg/cm2 | |||
| 抗拉屈服强度 | 80℃ | ASTM D-638 |
|
Kg/cm2 | |||
| 挠曲模量 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||
| 挠曲模量 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||
| 电气性能 | 介电强度 | 1/8" | ASTM D-149 |
|
KV/mm | ||
| 体积电阻率 | ASTM D-257 |
|
Ω.cm | ||||
| 热性能 | 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 |
|
℃ | ||
| 比热 |
|
Cal/g·℃ | |||||
| 线性热膨胀系数 | ASTM D-696 |
|
×10-5cm/cm/℃ | ||||
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 |
|
℃ | |||
| 熔点 | 差示扫描测热计DSC |
|
℃ | ||||
| 其它性能 | 强化含量 |
|
WT% | ||||